产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 吸水率 | | ASTM D-570 | 0.15-0.58 | % |
| 熔体流动速率 | | ASTM D-1238 | 10.5 | g/10min |
| 密度 | | ASTM D-792 | 0.043 | lb/in3 |
| 物理性能 | 阻燃性 | V-0 | UL 94 | 0.240 | inch |
| 比重 | | ASTM D-792 | 1.20 | |
| 阻燃性 | V-2 | UL 94 | 0.058 | inch |
| 模具收缩率 | | ASTM D-955 | 5-7 | in/inE-3 |
| 机械性能 | 压缩模量 | | ASTM D-695 | 345000 | Psi |
| 拉伸屈服强度 | | ASTM D-638 | 9000 | Psi |
| 拉伸断裂伸长率 | | ASTM D-638 | 110 | % |
| 洛氏硬度 | | ASTM D-785 | 70 | M scale |
| 屈服弯曲模量 | | ASTM D-790 | 340000 | Psi |
| 洛氏硬度 | | ASTM D-785 | 118 | R scale |
| 压缩强度 | | ASTM D-695 | 12500 | Psi |
| IZOD缺口冲击强度 | 73℉ | ASTM D-256 | 15 | ft-lb/in |
| IZOD无缺口冲击强度 | 73℉ | ASTM D-4812 | 60 | ft-lb/in |
| 拉伸屈服伸长率 | | ASTM D-638 | 7 | % |
| 剪切模量 | | ASTM D-4065 | 114000 | Psi |
| 剪切强度 | | ASTM D-732 | 6000 | Psi |
| 拉伸断裂强度 | | ASTM D-638 | 9500 | Psi |
| 屈服弯曲强度 | | ASTM D-790 | 13500 | Psi |
| 拉伸强度 | | ASTM D-1822 | 260 | ft-lb/in2 |
| 电气性能 | 损耗因数 | 60Hz | ASTM D-150 | 0.0009 | |
| 体积电阻率 | | ASTM D-527 | >1017 | Ω.cm |
| 介电强度 | | ASTM D-149 | 380 | V/mil |
| 损耗因数 | 1MHz | ASTM D-150 | 0.0100 | |
| 介电常数 | 60Hz | ASTM D-150 | 3.17 | |
| 介电常数 | 1MHz | ASTM D-150 | 2.96 | |
| 热性能 | 热变形温度 | 66Psi | ASTM D-648 | 280 | |
| 热传导率 | | ASTM C-177 | 0.19 | W/m.c |
| 维卡软化点 | | ASTM D-1525 | 310 | |
| 热变形温度 | 264Psi | ASTM D-648 | 270 | |
| 脆化温度 | | ASTM D-746 | 200 | |
| 其它性能 | 光传送 | | ASTM D-1003 | 88 | % |
| 混浊 | | ASTM D-1003 | 1.0 | % |
| 氧指数 | | ASTM D-2863 | 25 | % |
| 磨损 | | ASTM D-1044 | 10 | mg/1000cy |
| 折射指数 | | ASTM D-542 | 1.586 | |
产品信息：PC/沙伯基础(原GE)/243R
聚碳酸酯（Polycarbonate）缩写为PC是一种无色透明的无定形热塑性材料。其名称来源于其内部的CO3基团。主要生产原料为2,2-二（4-羟基苯基）丙烷（也称双酚A）。
物理性质：聚碳酸酯无色透明，耐热，抗冲击，阻燃，在普通使用温度内都有良好的机械性能。同性能接近聚甲基丙烯酸甲酯相比，聚碳酸酯的耐冲击性能好，折射率高，加工性能好，不需要添加剂就具有UL94 V-0级阻燃性能。但是聚甲基丙烯酸甲酯相对聚碳酸酯价格较低，并可通过本体聚合的方法生产大型的器件。随着聚碳酸酯生产规模的日益扩大，聚碳酸酯同聚甲基丙烯酸甲酯之间的价格差异在日益缩小。聚碳酸酯的耐磨性差。一些用于易磨损用途的聚碳酸酯器件需要对表面进行特殊处理。
化学性质：聚碳酸酯耐酸，耐油。聚碳酸酯不耐紫外光，不耐强碱。